9723 OBU
High Performance 9723 OBU Geomembrane
|
|
|
|
|---|---|---|
| Base Fabric Type |
Polyester |
|
| Base Fabric Weight (nominal) ASTM D751 |
3.65 oz/yd2 |
124 g/m2 |
| Coating Type |
Polyurethane Alloy |
|
| Weight ASTM D751 |
23 ± 2 oz/yd2 | 780 ± 102 g/m2 |
| Tongue Tear ASTM D751, 8 in (200mm) x 10in (250 mm) sample @ 12 in/min (5 mm/s) |
110/110 lbf | 489/489 N |
| Grab Tensile ASTM D751 |
350/400 lbf | 1557/1779 N |
| Strip Tensile ASTM D751 Procedure B |
275/325 lbf/in | 245/289 daN/5cm |
| Adhesion ASTM D751 Dielectric Weld ASTM D751 Hot Air Weld |
20 lbf/in 10 lbf/in |
18 daN/5 cm 9 daN/5 cm |
| Hydrostatic Resistance ASTM D751 Procedure A |
600 psi | 4.14 MPa |
| Bursting Strength (Ball) ASTM D751 |
750 lbf | 3336 N |
| Low Temperature ASTM D2136. 1/8 in (3 mm) mandrel, 4 hr |
Pass @ -65°F | Pass @ -54°C |
| Abrasion Resistance ASTM D3389 Taber Abrasion H-18 wheel, 1000 g load |
Face Side: 750 cycles | |
| Oil Resistance Mil-C-20696B |
Pass | Pass |
| Hydrocarbon Resistance Mil-C-20696B |
Pass | Pass |
Seaming: Thermal welding methodes are recommended. No glues or solvents are suggested.
We believe this information is the best currently available on the subject. We offer it as a suggestion in any appropriate experimentation you may care to undertake. It is subject to revision as additional knowledge and experience are gained. We make no guarantee of results and assume no obligation or liability whatsoever in connection with this information. In case of conflict between standard and metric specifications, standard shall apply.